The conventional corrosion resistance method of galvanized cable bridge stand:

　　1：熱浸鍍鋅 鋅在耐腐蝕上有著出眾的效果，鍍鋅的原理是在于鍍層破損或遭腐蝕生成Fe-Zn原電池時，鋅鍍層屬于陽出彩性鍍層，鋅犧牲溶解，保護(hù)了鋼鐵。因此鋼鐵上的鍍鋅層不是單純的機(jī)械保護(hù)作用，而是通過電化學(xué)作用保護(hù)基體免遭腐蝕，即使鋅層不完整也會起到這個作用。這是一種犧牲陽出彩來保護(hù)陰出彩金屬的辦法，壽命就在于它的腐蝕鋅鍍層的阻力以及腐蝕速度。通常熱浸鍍鋅的厚度在6um以上，鋅和鐵的接觸面結(jié)合成了一層鋅鐵合金，提高了鋅的附著性，國外也專門為這一發(fā)現(xiàn)進(jìn)行了考究，在不同環(huán)境下的熱浸鍍鋅進(jìn)行了大氣露出實(shí)驗(yàn)，研究表明這種方法適合針對防腐使用，所以大家可以盡量選擇鍍鋅橋架。鑒道橋架即是運(yùn)用了這種處理方法。

　　1: hot dip galvanized zinc has great effect on the corrosion resistance, that is, the principle of galvanized coating damage or corrosion generated by Fe - zinc galvanic, zinc coating belongs to the anode sex coating, zinc sacrifice to dissolve, to protect the steel. So the zinc coating on the steel was not a simple mechanical protection, but rather through electrochemical action to protect substrate from corrosion, even if incomplete zinc layer will play the role. This is a way of protecting the cathode metal from the anode, which is the resistance and corrosion of the zinc coating. Usually the thickness of the hot dip galvanized above 6 um, zinc and iron in the contact area combine into a layer of zinc iron alloy, improves the adhesion of zinc, abroad specifically for the fastidious, the discovery in a different environment atmosphere above experiments, the hot dip galvanizing of research shows that this method is most suitable for used for corrosion protection, so we can try to choose galvanized bridge. The bridge is used for this treatment.

　　2.涂防銹漆：又名“噴塑電纜橋架”，因?yàn)橛行┏叽邕^大的鍍鋅橋架受到一定的設(shè)備限制，所以通常會運(yùn)用操作簡單方便的涂防銹漆。防銹漆由紅丹防銹漆、鐵紅酚醛防銹漆、鋅黃防銹漆等防銹漆，作用效果一般，防腐作用不強(qiáng)，為了保證工程的整個安全性以及使用效果，建議不使用這種方法。

　　2. Coating antirust paint, also known as "plastic cable tray, because some size is too large galvanized bridge is limited by certain equipment, so often use the most simple and convenient operation with anticorrosive paint. Antirust paint the red lead, iron oxide red phenolic anti-rust paint, zinc yellow antirust paints such as antirust paint, effect, corrosion protection is not strong, in order to guarantee the whole engineering safety and using effect, suggest don't use this method.

　　3.電鍍鋅：電鍍鋅的操作過程中，比熱浸鍍鋅更簡單，本錢相比之下也比較低，它撇棄了傳統(tǒng)方式的水電鍍，真空鍍，現(xiàn)在的方式更加的環(huán)保。在歷來工業(yè)上，電鍍等處理的工藝排出的廢液是非常污染環(huán)境和影響人體的，但是該工業(yè)已經(jīng)實(shí)現(xiàn)了環(huán)保的技術(shù)。電鍍鋅的厚度一般在6um左右，實(shí)際上來說不太適合要求非常高的防腐蝕工程上。

　　3. Electricity galvanized, electric galvanized the operation of the process, the specific heat galvanizing is more simple, the capital, by contrast is low, it abandoned the traditional way of water plating, vacuum plating, now way more environmentally friendly. In the traditional industry, the waste liquor from the process of electroplating and other processing is very polluting and affecting the human body, but the industry has already achieved the environmental protection technology. The thickness of electrogalvanizing is generally around 6um, which is not very suitable for very high corrosion prevention engineering.

　　以上介紹希望對您有所幫助，我們的產(chǎn)品質(zhì)量好，價格合理，真誠歡迎大家來選購，我們竭誠為您服務(wù)。

　　The above introduction hope is helpful to you, our product quality is good, the price is reasonable, sincerely welcome you to choose and buy, we wholeheartedly serve for you.